====== Foams ====== | ====== Foams ====== | ||
+ | |||
+ | 3/8" (10 mm) thick seems to work well for putting DIPs on both sides | ||
This section was added to try to learn why some black conductive foams degrade into powder and others degrade into a (mildly corrosive?) sticky mess | This section was added to try to learn why some black conductive foams degrade into powder and others degrade into a (mildly corrosive?) sticky mess | ||
Line 171: | Line 173: | ||
* Insulative: surface resistance > 1 x 10 12 ohms/square | * Insulative: surface resistance > 1 x 10 12 ohms/square | ||
* Anti-static: | * Anti-static: | ||
+ | |||
+ | |||
+ | https:// | ||
+ | * Too low density to be useful | ||
+ | * Open cell | ||
+ | * 1.4 lbs. cu. ft | ||
+ | |||
+ | < | ||
+ | depends on whether you want your foam to turn to goo or powder. personally i prefer goo | ||
+ | 14:57:57 powder is open cell foam, it works as an abrasive too | ||
+ | 14:58:07 goo is closed cell foam, which is oddly slick | ||
+ | 14:58:23 after 20 years the foams disintegrate | ||
+ | 14:58:41 open cell foam turns into some sort of acid (acetic?) which will eat chip legs i think | ||
+ | 14:58:45 i don't know about closed cell | ||
+ | 14:58:56 i think closed cell disintegrates much slower but gets ' | ||
+ | </ | ||
===== Density ===== | ===== Density ===== |