 Slightly a step up is to use a machine without a jig.  Some notes: [[:tutorial:lapping|tutorial]]
+====== mcmaster notes ======
+g Al round block
+  * P180 / 80 um used SiC: 140 mm3 / sec @ speed 3
+    * 460 - 423 = 37 um / min
+    * 5.3 x 11.0 mm = 58.3 mm2
+    * 37 * 4 * 58.3 = 8628.4 mm3 / min
+    * One die fractured after just one minute
+    * Probably too aggressive to use in practice
+  * 30 um new AO: 6.2 mm3 / sec @ speed 3
+    * Same area as above
+    * 1.6 um / min
+    * 1.6 * 4 * 58.3 = 373 mm3 / min
+Removing pads
+  * 300 F optimal
+  * By 350F glue is too soft to come off in one piece